江苏春晨电缆有限公司专业生产EV-EF充电桩电缆，充电桩电缆可在室内或室外使用，室外使用时充电桩电缆应满足高寒、日光、雨水以及汽车用油类物质的侵蚀，这就要求电缆具备适用于使用场合的抗紫外线、臭氧、耐高低温和化学侵蚀等特殊性能，Antimony flame retardant

Advantages: three oxidation of two antimony can not be used as a flame retardant, and with the appropriate use of halogen compounds, can play a particularly effective flame retardant performance. Disadvantages of antimony flame retardant synergistic mechanism of heavy metals, toxic, and arsenic homologues in crude product containing arsenic and other heavy metals, arsenic trioxide. Can not be used as green filler and green flame retardant.

二、*阻燃剂（ATH）

Two, aluminum hydroxide flame retardant (ATH)

优点：价格低，阻燃性好。

Advantages: low price, good flame retardancy.

Disadvantages: poor heat resistance, 200 degrees to dehydration, 330 C and 350 C is compley dehydrated, and the curing of the resin in the aluminum hydroxide dehydration temperature range, thus leading to the synthesis of resin foam, decrease surface unevenness, dielectric properties, low rate of finished products. Applied to the high temperature caused by silica gel fog, white foam products, such as dielectric decline. EC is 60~100 S/cm, easy to absorb moisture.

三、*阻燃剂

Three, magnesium hydroxide flame retardant

优点：*阻燃剂的应用（430℃分解）无毒

Advantages: application of magnesium hydroxide flame retardant (430 DEG C decomposition) non-toxic

缺点： 不耐酸，醋酸都能将*溶解，只适合做低档产品。易吸潮，分散差，介电性差。

Disadvantages: not acid, acetic acid can be dissolved in magnesium hydroxide, only suitable for low-grade products. Easy to absorb moisture, poor dispersion, poor dielectric properties.

四、高耐热勃姆石阻燃剂（Boehmite, ALOOH）EV-EF充电桩电缆

Four, high heat-resistant boehmite flame retardants (Boehmite, ALOOH)

优点：1%脱水温度达350℃以上，500℃脱水达到峰值，EC<50μS/cm，介电性强，解决了*因脱水温度低而导致产品缺陷及介电性降低的问题，耐酸碱性强。

Advantages: 1% dehydration temperature above 350 degrees, 500 degrees of dehydration peak, EC<50 S/cm, dielectric, solves the low temperature caused by dehydration of aluminum hydroxide product defects and dielectric properties decreased, acid and alkali resistance.

Disadvantages: flame retardant slightly lower than aluminum hydroxide, flame retardant performance to achieve the same need to add. However, its biggest feature is high heat resistance, both thermal conductivity, acid and alkali resistance, made of high heat resistance functional materials can improve the added value of the product.